Novel analytical techniques for the assessment of degradation of silicone elastomers in high voltage applications
Sovar, Robert D. (2005) Novel analytical techniques for the assessment of degradation of silicone elastomers in high voltage applications. Masters by Research thesis, Queensland University of Technology.
Over the last 20 years "composite" insulators have been increasingly used in high voltage applications as an alternative traditional materials. More recently, polydimethylsiloxane (PDMS) have been used as weather sheds on these composite insulators. The main attraction with PDMS is that the surface hydrophobicity can be recovered following pollution or surface discharges. Among the possible mechanisms for recovery the most likely is the migration of low molecular weight silicone oil (LMWS) from the bulk to the surface encapsulating pollutant particles. Although it is widely recognised that the migration of LMWS is the cause of this recovery of hydrophobicity, the mechanism of what actually occurs is not well understood. It is also not known for how long this process will continue.
The main objective of this study program was to gain improved understanding of the surface hydrophobic recovery process that is unique to polydimethlysiloxane high-voltage insulators. Fundamental knowledge of this mechanism has been increased through the development of the Contact Angle DRIFT Electrostatic Deposition (CADED) novel analytical technique. This technique enabled study of the degradation of silicone elastomers subjected to high voltage environments by closely following LMWS migration from the bulk material to the surface and linking it to the contact angle measurements. The migration rate data showed that the aged material recovered faster that the virgin material. Differences in the rate and maximum surface levels of silicone were seen between materials from different manufacturers. This has significant implications for the life-time of these materials
A model system has been developed to examine LMWS diffusion through the bulk material and into the interface of surface and pollutant. This was achieved by examining theoretical and empirically derived equations and using existing experimental data to better understand the mechanism of recovery. This diffusion was Fickian in the initial stages of recovery.
X-ray photoelectron spectroscopy (XPS) and contact angle measurements were used to substantiate the degree of degradation in in-field silicone insulators by quantifying the levels of the major degradation products: silica and silica-like material and alumina.
Impact and interest:
Citation counts are sourced monthly from and citation databases.
These databases contain citations from different subsets of available publications and different time periods and thus the citation count from each is usually different. Some works are not in either database and no count is displayed. Scopus includes citations from articles published in 1996 onwards, and Web of Science® generally from 1980 onwards.
Citations counts from theindexing service can be viewed at the linked Google Scholar™ search.
Full-text downloads displays the total number of times this work’s files (e.g., a PDF) have been downloaded from QUT ePrints as well as the number of downloads in the previous 365 days. The count includes downloads for all files if a work has more than one.
|Item Type:||QUT Thesis (Masters by Research)|
|Supervisor:||George, Graeme & Cash, Gregory|
|Keywords:||Composite insulators, polydimethylsiloxane (PDMS), low molecular weight silicone oil (LMWS), polydimethlysiloxane high-voltage insulators, Contact Angle DRIFT Electrostatic Deposition (CADED), hydrophobicity, Silicone Elastomers, high voltage, applications|
|Divisions:||Past > QUT Faculties & Divisions > Faculty of Science and Technology|
|Department:||Faculty of Science|
|Institution:||Queensland University of Technology|
|Deposited On:||03 Dec 2008 03:56|
|Last Modified:||28 Oct 2011 19:42|
Repository Staff Only: item control page