Artificial grain boundary Josephson junctions : properties and applications

Ivanov, Z.G., Alarco, J.A., Claeson, T., Nilsson, P.aaA, Olsson, E., Olsson, H.K., Stepantsov, E.A., Tzalenchuk, A.Ya, & Winkler, D. (1993) Artificial grain boundary Josephson junctions : properties and applications. In Proceedings of the Beijing International Conference : High Temperature Superconductivity (BHTSC '92). World Sci, p. 722.

View at publisher

Abstract

Engineered grain boundary Josephson junctions in YBaCuO were formed on bicrystal Y-ZrO2 substrates. Laser deposited films were patterned into micron size microbridges. The authors obsd. a pronounced correlation between superconducting transport properties of grain boundary junctions and the misorientation angle θ between the two halves of the bicrystal. The crit. Josephson current Ic decreased about four orders of magnitude as θ was increased from 0 to 45 degrees. Clear microwave and magnetic field responses were obsd. at 77 K. At this temp., crit. current times normal resistance products, IcRn, of up to 1 mV were measured for low angle grain boundaries, and Shapiro steps were obsd. up to that voltage. DC SQUIDs were fabricated, and best performance at 77 K was obtained for θ = 32° with a 4-μm strip width. To utilize the higher IcRn value of a lower θ, submicron junctions have to be developed. [on SciFinder(R)]

Impact and interest:

Search Google Scholar™

Citation counts are sourced monthly from Scopus and Web of Science® citation databases.

These databases contain citations from different subsets of available publications and different time periods and thus the citation count from each is usually different. Some works are not in either database and no count is displayed. Scopus includes citations from articles published in 1996 onwards, and Web of Science® generally from 1980 onwards.

Citations counts from the Google Scholar™ indexing service can be viewed at the linked Google Scholar™ search.

ID Code: 64075
Item Type: Book Chapter
Additional Information: CAPLUS AN 1994:336328(Conference)
Keywords: grain boundary Josephson junction cuprate superconductor, yttrium barium cuprate Josephson junction, yttria stabilized zirconia substrate Josephson junction, bicrystal zirconia substrate Josephson junction
Divisions: Current > Institutes > Institute for Future Environments
Deposited On: 06 Nov 2013 23:02
Last Modified: 06 Nov 2013 23:03

Export: EndNote | Dublin Core | BibTeX

Repository Staff Only: item control page