Effect of heat treatment and bend strain on the Jc of Ag-sheathed Bi-2212 tape

Yamashita, T., Ilyushechkin, A.Y., & Talbot, P.C. (2000) Effect of heat treatment and bend strain on the Jc of Ag-sheathed Bi-2212 tape. Superconductor Science and Technology, 13(12), p. 1575.

View at publisher

Abstract

Bi-2212 tapes were fabricated using a powder-in-tube method and their superconducting properties were measured as a function of heat treatment. The tapes were heated to temperature, T1 (884-915 °C), and kept at that temperature for 20 min to induce partial (incongruent) melting. The samples were cooled to T2 with a ramp rate of 120 °C h-1 and then slowly cooled to T3 with a cooling rate, R2, and from T3 to T4 with a cooling rate, R3. The tapes were kept at the temperature T4 for P1 hours and then cooled to room temperature. Both R1 and R2 were chosen between 2 and 8 °C h-1. It was found that the structure and Jc of the tapes depend on the sintering conditions, i.e. T1-4, R1-3 and P1. The highest Jc of 5800 Å cm-2 was obtained at 77 K in a self-field with heat treatment where T1 = 894 and 899 °C, R1 = R2 = 5 °C h-1 and P1 = 6 h were employed. When 0.7% of bend strain, which is equivalent to a bend radius of 5 mm, was applied to the tape, 80% of the initial Jc was sustained.

Impact and interest:

0 citations in Scopus
Search Google Scholar™
1 citations in Web of Science®

Citation counts are sourced monthly from Scopus and Web of Science® citation databases.

These databases contain citations from different subsets of available publications and different time periods and thus the citation count from each is usually different. Some works are not in either database and no count is displayed. Scopus includes citations from articles published in 1996 onwards, and Web of Science® generally from 1980 onwards.

Citations counts from the Google Scholar™ indexing service can be viewed at the linked Google Scholar™ search.

ID Code: 64508
Item Type: Journal Article
Refereed: Yes
Additional URLs:
DOI: 10.1088/0953-2048/13/12/302
ISSN: 1361-6668
Subjects: Australian and New Zealand Standard Research Classification > PHYSICAL SCIENCES (020000)
Australian and New Zealand Standard Research Classification > CHEMICAL SCIENCE (030000)
Divisions: Current > Schools > School of Chemistry, Physics & Mechanical Engineering
Current > Institutes > Institute for Future Environments
Current > QUT Faculties and Divisions > Science & Engineering Faculty
Copyright Owner: Copyright 2000 IOP Publishing Ltd
Deposited On: 14 Nov 2013 23:57
Last Modified: 14 Nov 2013 23:57

Export: EndNote | Dublin Core | BibTeX

Repository Staff Only: item control page